Archives: Alloys

Published on October 30, 2017

Composition Copper: 55%, Nickel: 45% Resistance 294 ohm-cir-mil/ft 0.0000490 ohm-cm Maximum Recommended Operating Temperature 1022° F 550° C Melting Point 2201° F 1205° C Density ( @ 20.0° C/ 68.0° F) 0.321 lb/in³ 8.89 g/cc Tensile Strength, Ultimate, Annealed 60000 psi 414 MPa Tensile Strength, Ultimate, Hard Drawn 140000 psi 965 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Iron: 74%, Chromium: 18%, Nickel: 8% Resistance 433 ohm-cir-mil/ft 0.0000720 ohm-cm Maximum Recommended Operating Temperature 1112° F 600° C Melting Point 2642° F 1450° C Density ( @ 20.0° C/ 68.0° F) 0.286 lb/in³ 7.92 g/cc Tensile Strength, Ultimate, Annealed 100000 psi 689 MPa Tensile Strength, Ultimate, Hard Drawn 220000 psi 1517 MPa Temperature […]

Published on October 30, 2017

Composition Nickel: 60%, Iron 24%, Chromium 16% Resistance 675 ohm-cir-mil/ft 0.000112 ohm-cm Maximum Recommended Operating Temperature 1850° F 1010° C Melting Point 2534° F 1390° C Density ( @ 20.0° C/ 68.0° F) 0.298 lb/in³ 8.25 g/cc Tensile Strength, Ultimate, Annealed 95000 psi 655 MPa Tensile Strength, Ultimate, Hard Drawn 175000 psi 1207 MPa Temperature […]

Published on October 30, 2017

Composition Nickel: 80%, Chromium: 20% Resistance 650 ohm-cir-mil/ft 0.000108 ohm-cm Maximum Recommended Operating Temperature 2147° F 1175° C Melting Point 2552° F 1400° C Density ( @ 20.0° C/ 68.0° F) 0.304 lb/in³ 8.41 g/cc Tensile Strength, Ultimate, Annealed 100000 psi 689 MPa Tensile Strength, Ultimate, Hard Drawn 200000 psi 1379 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Nickel: 75%, Chromium 20%, Aluminium: 2.5%, Copper: 2.5% Resistance 800 ohm-cir-mil/ft 0.000134 ohm-cm Maximum Recommended Operating Temperature 572° F 300° C Melting Point 2462° F 1350° C Density ( @ 20.0° C/ 68.0° F) 0.293 lb/in³ 8.10 g/cc Tensile Strength, Ultimate, Annealed 120000 psi 827 MPa Tensile Strength, Ultimate, Hard Drawn 240000 psi 1655 […]