Archives: Alloys

Published on October 30, 2017

Composition Chromium: 21%, Aluminium: 5.5%, Iron: Balance Resistance 875 ohm-cir-mil/ft 0.000145 ohm-cm Maximum Recommended Operating Temperature 2354° F 1290° C Melting Point 2768° F 1520° C Density ( @ 20.0° C/ 68.0° F) 0.257 lb/in³ 7.10 g/cc Tensile Strength, Ultimate, Annealed 120000 psi 827 MPa Tensile Strength, Ultimate, Hard Drawn N/A N/A Temperature Coefficient of […]

Published on October 30, 2017

Composition Chromium: 22.5%, Aluminium: 4.6%, Iron: Balance Resistance 815 ohm-cir-mil/ft 0.000135 ohm-cm Maximum Recommended Operating Temperature 2138° F 1170° C Melting Point 2768° F 1520° C Density ( @ 20.0° C/ 68.0° F) 0.262 lb/in³ 7.25 g/cc Tensile Strength, Ultimate, Annealed 105000 psi 724 MPa Tensile Strength, Ultimate, Hard Drawn N/A N/A Temperature Coefficient of […]

Published on October 30, 2017

Composition Copper: 88%, Nickel: 12% Resistance 90 ohm-cir-mil/ft 0.0000150 ohm-cm Maximum Recommended Operating Temperature 752° F 400° C Melting Point 1994° F 1090° C Density ( @ 20.0° C/ 68.0° F) 0.321 lb/in³ 8.89 g/cc Tensile Strength, Ultimate, Annealed 35000 psi 241 MPa Tensile Strength, Ultimate, Hard Drawn 75000 psi 517 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Copper: 94%, Nickel: 6% Resistance 60 ohm-cir-mil/ft 0.00000997 ohm-cm Maximum Recommended Operating Temperature 572° F 300° C Melting Point 1994° F 1090° C Density ( @ 20.0° C/ 68.0° F) 0.321 lb/in³ 8.89 g/cc Tensile Strength, Ultimate, Annealed 35000 psi 241 MPa Tensile Strength, Ultimate, Hard Drawn 70000 psi 483 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Copper: 98%, Nickel: 2% Resistance 30 ohm-cir-mil/ft 0.00000499 ohm-cm Maximum Recommended Operating Temperature 392° F 200° C Melting Point 1994° F 1090° C Density ( @ 20.0° C/ 68.0° F) 0.321 lb/in³ 8.89 g/cc Tensile Strength, Ultimate, Annealed 30000 psi 207 MPa Tensile Strength, Ultimate, Hard Drawn 60000 psi 414 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Copper: 100% Resistance 10 ohm-cir-mil/ft 0.00000166 ohm-cm Maximum Recommended Operating Temperature 302° F 150° C Melting Point 1981° F 1083° C Density ( @ 20.0° C/ 68.0° F) 0.323 lb/in3 8.93 g/cc Tensile Strength, Ultimate, Annealed 30500 psi 210 MPa Tensile Strength, Ultimate, Hard Drawn 65000 psi 448 MPa Temperature Coefficient of Resistance 0.0000173 […]

Published on October 30, 2017

Composition Nickel: 99.5% Resistance 57 ohm-cir-mil/ft 0.00000948 ohm-cm Maximum Recommended Operating Temperature 932° F 500° C Melting Point 2642° F 1450° C Density ( @ 20.0° C/ 68.0° F) 0.321 lb/in³ 8.89 g/cc Tensile Strength, Ultimate, Annealed 60000 psi 414 MPa Tensile Strength, Ultimate, Hard Drawn 135000 psi 931 MPa Temperature Coefficient of Resistance 0.00470 […]

Published on October 30, 2017

Composition Nickel: 70%, Iron: 30% Resistance 120 ohm-cir-mil/ft 0.0000199 ohm-cm Maximum Recommended Operating Temperature 1112° F 600° C Melting Point 2597° F 1425° C Density ( @ 20.0° C/ 68.0° F) 0.305 lb/in³ 8.44 g/cc Tensile Strength, Ultimate, Annealed 70000 psi 483 MPa Tensile Strength, Ultimate, Hard Drawn 150000 psi 1034 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Copper: 78%, Nickel: 22% Resistance 180 ohm-cir-mil/ft 0.0000299 ohm-cm Maximum Recommended Operating Temperature 932° F 500° C Melting Point 1994° F 1090° C Density ( @ 20.0° C/ 68.0° F) 0.321 lb/in³ 8.89 g/cc Tensile Strength, Ultimate, Annealed 50000 psi 345 MPa Tensile Strength, Ultimate, Hard Drawn 100000 psi 689 MPa Temperature Coefficient of […]

Published on October 30, 2017

Composition Copper: 84%, Manganese: 12%, Nickel: 4% Resistance 290 ohm-cir-mil/ft 0.0000482 ohm-cm Maximum Recommended Operating Temperature 572° F 300° C Melting Point 1868° F 1020° C Density ( @ 20.0° C/ 68.0° F) 0.296 lb/in³ 8.19 g/cc Tensile Strength, Ultimate, Annealed 70000 psi 483 MPa Tensile Strength, Ultimate, Hard Drawn 150000 psi 1034 MPa Temperature […]